[en] Phase and isotope equilibrium in the systems ZrV2-xNix-H2(D2), where x = 0.1-0.4, was studied in the temperature range of 273-323 K. Sorption isotherms were obtained for protium and deuterium, thermodynamic characteristics of hydride formation and hydrogen isotopes separation factor being determined. It was ascertained that introduction of small additions of nickel involves increase in hydride formation pressure and hydrogen isotopes separation factor along with insignificant reduction of intermetallic compound (IMC) capacity in terms of hydrogen. Analysis of the results obtained was carried out relying on the theory of hydrogen isotopes separation previously developed by the authors, consisting in sorption in metals and IMC with filling positions of different types (multiposition filling)
[ru]
В диапазоне температур 273-323 К исследовано фазовое и изотопное равновесие в системах ZrV2-xNix-H2(D2), где x = 0.1-0.4. Для протия и дейтерия получены изотермы сорбции, определены термодинамические характеристики гидридообразования и коэффициент разделения изотопов водорода. Установлено, что введение небольших добавок никеля приводит к увеличению давления гидридообразования и коэффициента разделения изотопов водорода при одновременном незначительном уменьшении емкости интерметаллического соединения (ИМС) по водороду. Анализ полученных результатов проведен с использованием разработанной авторами ранее теории разделения изотопов водорода при сорбции в металлах и ИМС с заполнением позиций различного типа (многопозиционным заполнением)Journal