[en] Vitrification of cesium loaded inorganic ion exchangers (mordenite type molecular sieves/zeolite AR-1) was studied empolying borosilicate glass systems. Direct vitrification of aluminosilicates is rather difficult mainly on account of volatility of cesium at processing temperatures of 1100 degC-1300 degC. In the borosilicate glass system, oxides of lead, sodium and zinc along with boric oxide were employed as major glass formers. Homogeneous glass matrix was obtained incorporating simulated composition of mordenite along with oxides of sodium, lead and boron at the processing temperature of 950 degC. The waste oxide loading up to 50% on dry weight basis was incorporated in this glass formulation. Partial replacement of PbO by TeO₂, Bi₂O₃ and CaF₂ resulted in lowering of the processing temperature and also increasing homogeneity of matrix. Based on these results, a glass matrix was prepared with actual cesium AR-1 molecular sieves with processing temperature limited to 925 degC. Powdered samples of glass matrix were subjected to leaching as per ASTM-1285 Product Consistency Test in high purity water at 90 degC for 28 days. The normalised cesium leach rate of this glass was found to be 3.92 x 10^-6 g/cm²/day, which is comparable to sodium borosilicate glass matrices currently in use for immobilisation of high level waste. The molecular sieves are also amenable to immobilization in cement matrix. As expected, there is substantial volume reduction by factor 3 in vitrification compared to their immobilization in cementious matrices. Also the quantity of cesium leached from vitrified product was nearly 10,000 times lower compared to cement based matrix. Vitrification of mordenite molecular sieves would lead to high capacity utilisation of zeolite AR-1 for the treatment of low and intennediate levelliquid effluents. (author)