[en] The physicochemical processes, taking place by the RuAl alloy formation from the ruthenium and aluminium powder mixture within the temperature range of 250-1400 deg C in the vacuum from 10-2 up to 10-5 mm mercury column are studied on the alloys of the Ru50Al50 stoichiometric and Ru52Al48 hyperstoichiometric composition. The Ru + Al → RuAl interaction with the exothermal effect begins in the solid phase at the temperatures below the aluminium tmelt. The Ru2Al3, RuAl2 and RuAl traces rich in aluminium are formed already at 600 deg C; at 1000-1400 deg C the RuAl becomes the basic phase; the precipitates of the ruthenium-based solid solution are additionally present in the hyperstoichiometric Ru52Al48 alloy. The Ru52Al48 crystalline lattice period increases with the growth of the caking temperature from 0.29906 (660 deg C) up to 0.22955 nm (1400 deg C). The Al2O3 inclusions up to 1 μm in diameter are identified in the caked alloys in vacuum after the reaction caking
[ru]
На сплавах стехиометрического Ru50Al50 и гиперстехиометрического Ru52Al48 составов изучены физико-химические процессы, происходящие при сплавообразовании RuAl из смеси порошков рутения и алюминия в интервале температур 250-1400 град С в вакууме от 10-2 до 10-5 мм рт. ст. Взаимодействие Ru + Al → RuAl с экзотермическим эффектом начинается в твердой фазе при температурах ниже tпл алюминия. Уже при 600 град С образуются богатые алюминием Ru2Al3, RuAl2 и следы RuAl, при 1000-1400 град С RuAl становится основной фазой; в гиперстехиометрическом сплаве состава Ru52Al48 дополнительно присутствуют выделения твердого раствора на основе рутения. Период кристаллической решетки Ru52Al48 с повышением температуры спекания увеличивается от 0.29906 (660 град С) до 0.29955 нм (1400 град С). После реакционного спекания в вакууме в спеченных сплавах обнаружены включения Al2O3 диаметром до 1 мкмJournal