[en] Piezoelectric, dielectric and physicomechanical properties of polymeric piezocomposites on piezoceramics basis are one of the major operational devices of applications. During their application in various devices for a long time can be exposed to various influences for a long time. Piezoelectric, dielectric and strength properties of polymeric piezocomposites strongly depend from the interphase phenomena, and also on charges saved up on border of the unit between components of a composition. Therefore creation the preliminary centers localization for charges in a composition is an actual problem for development effective polymeric piezocomposites. In the given work results of a research preliminary discharge processing's of powders of polymer on strength properties and dielectric characteristics of polymeric compositions on a basis polyvinilidenftorid (PVDF), high density polyethylene and piezoceramic from tetragonal structure are poisoned. Piezoceramic had structure plumbum-zirconate-titanate (PZT). Powders of polymer have been subjected to discharge processing in a quartz glass tube with a diameter 15 mm which walls with 1 mm. It is earthed, from one end and to other end it is connected with high-voltage electrode. Compositions in a volumetric ratio of 90+10 % have been obtained at temperature 435Κ under pressure 15ΜΠa. After creation reception of samples they were exposed electrothermopolarization. It is experimentally established, that after discharge processing powders of polymer depending on of processing duration electric and mechanical durability, and also an accrued charge on border of the unit of phases up to the certain value increases, and then decreases. Also it is shown, hat influence of category processing on strength and dielectric characteristics of a composition on the basis of polymer PVDF is more than , has on polyethylene basis. Changes piezoelectric, dielectric it is supposed, that, and strength properties to an extreme piezocomposite depend on a time of discharge processing is connected by changes of a are formed charging conditions, i.e. as a result of oxidizing processes traps for charges