[en] To study surface behaviors, MgFe₂O₄ ferrite materials having different grain sizes were synthesized by two different chemical methods, i.e., a polymerization method and a reverse coprecipitation method. The single phase of the cubic MgFe₂O₄ was confirmed by the X-ray diffraction method for both the precursors decomposed at 600-1000 deg. C except for a very small peak of Fe₂O₃ was detected for the samples calcined at 600 and 700 deg. C by the polymerization method. The crystal size and particle size increased with an increase in the sintering temperature using both methods. The conductance of the MgFe₂O₄ decreased when the atmosphere was changed from ambient air to air containing 10.0 ppm NO₂. The conductance change, C = G(air)/G(10 ppm NO₂), was reduced with an increase in the operating temperature. For the polymerization method, the maximum C-value was ca. 40 at 300 deg. C for the samples sintered at 900 deg. C. However, the samples sintered at 1000 deg. C showed a low conductance change in the 10 ppm NO₂ gas, because the ratio of the O₂ gas adsorption sites on the particle surface is smaller than those of the samples having a high C-value. The low Mg content on the surface affects the low ratio of the gas adsorption sites. For the reverse coprecipitation method, the particle size was smaller than that of the polymerization method. Although a stable conductance was obtained for the sample sintered at 900 and 1000 deg. C, its conductance change was less than that of the polymerization method