[en] The isotactic polypropylene is a linear polymer which exhibits low melt strength. Irradiation of PP under inert atmosphere causes a combination of chain scissioning and long-chain branching, and results in a material with significant enhanced melt strength. This process, which is sometimes termed visbreaking, thus provides improvement of rheological properties. HMS-PP (High Melt Strength Polypropylene) was obtained by the irradiation in atmosphere of acetylene as crosslinker agent. It was employed doses of 12.5 and 20 kGy of gamma radiation. The objective of this study is to investigate the effects of thermal ageing on the crystallinity level and chemical structure of HMS-PP. The thermal stability of the HMS-PP was evaluated after thermal ageing of samples using a stove at temperature of 90 deg C, in presence of air at different periods of time. The samples submitted to the thermal ageing were characterized by: thermogravimetry (TGA), differential scanning calorimetry (DSC), infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). Since the long-term engineering properties of HMS-PP are intrinsically linked with the polymer microstructure, there is significant interest in understanding the effects of ageing, particularly due to prolonged exposure at service temperatures. In thermo-oxidative conditions, the formation of the oxidation products essentially involves a hydrogen abstraction by the peroxyl radicals, leading to hydroperoxides as primary products and chemical degradation in the immediate crack tips. Oxidative degradation on the network of HMS-PP, created by radiation process of PP, was revealed by the analytical results showing the susceptibility of HMS-PP to thermal oxidative degradation. Yellowing of the samples surface and oxidative products of degradation among other evidences were observed. (author)