[en] The polyvinyl chloride (PVC) is a technological and low cost polymer, however it presents high sensitivity to high energy irradiation because of the weakness of carbon-chloride bond face to carbon-carbon and carbon-hydrogen bonds. Grafting is a type of co-polymerization process that can allow it an increase of mechanical characteristics. The aim of this work is to evaluate the mechanical properties of styrene grafted PVC by electron beam irradiation using mutual and pre-irradiation methods to verify the mechanical resistance changes of obtained product whether grafting process is applied from non-irradiated or from pre-irradiated substrates. The irradiation procedures were performed in atmosphere air or inert atmosphere and the irradiation conditions comprised doses from 10 kGy to 100 kGy and dose rates of 2.2 kGy/s and 22.4 kGy/s. The styrene grafted samples were analyzed by gravimetry to determinate the grafting yield; the final values have been averaged from a series of three measurements. The Mid-A TR-FTIR was the spectrophotometer technique used for qualitative/semi-quantitative analysis of grafted samples. The Young's module and tensile strength of pre-irradiated and grafted PVC samples at both methods were measured at a Lloyd LXR tensile tester at a cross-head speed of 10.00 mm/min. We observed the decrease of Young's module and tensile strength with the increase of absorbed dose at pre-irradiated PVC samples. These mechanical parameters results are discussed. (author)