[en] During 2006 the development of high and low-pH cementitious grouts for fractures > 100 μm designed for the ONKALO rock was continued within the LPHTEK/IMAproject. The main focus in laboratory was to study high pH micro cement grouts. The low pH (≥ 11.0) of the cementitious grout material is required in deep repository as natural pH plume deriving from pure cement paste is very high and moves via ground water circulation in bedrock. This may be deleterious to the protective covers of nuclear waste. The objective to study high pH grouts in laboratory was to optimise their composition and to get preliminary test results. Low pH grouts based on Portland cement + micro silica were also studied further in laboratory to understand their behaviour more thoroughly in different conditions and due to quality changes in materials and to compare the laboratory results with the field results. Alternative fine-grained glass material was briefly studied to replace silica in low pH grout. Low and high pH rock bolt mortars were also developed and tested to get the preliminary test results. The results of the 2006 laboratory work are presented in this report. The high pH micro cement mix U1 with no silica, mix 5/5 with moderate silica and low pH mix P308B rich in silica show generally good properties at fresh and hardening stage at +12 deg C. Lower temperature gives weaker strength build-up with all the mixes and weakens especially the Marsh fluidity and penetration ability of the mixes 5/5 and P308B as bulk density rises a little at lower temperature. Cement quality variation and insufficient mixing may also weaken the properties of all mixes. Deformation of the hardened mixes was observed in laboratory tests. This may weaken their durability if cracks are formed in the grouts at later ages and need to be studied more thoroughly. (orig.)