[en] Corrosion, Fatigue and Irradiation embrittlement are the major degradation mechanisms responsible for ageing of RPV (and its internals) of a Pressurized Water Reactor. While corrosion and fatigue can generate cracks, irradiation damage can lead to brittle fracture initiating from these cracks. Ageing in nuclear power plants needs to be managed so as to ensure that design functions remain available throughout the life of the plant. From safety perspective, this implies that ageing degradation of systems, structures and components important to safety remain within acceptable limits. Reactor Pressure Vessel has been identified as the highest priority key component in plant life management for Pressurized Water Reactors. Therefore special attention is required to ensure its structural integrity during its lifetime. In this paper, structural integrity assessment for typical VVER-1000 RPV is carried out under severe accidental cool down transients using the Finite Element Method. Three different accidental scenarios are postulated and safety of the vessel is conservatively assessed under these transients using the Linear Elastic Fracture Mechanics approach. Transient thermo mechanical stress analysis of the core belt region of the RPV is carried out in presence of postulated cracks and stress intensity factors are calculated and compared with the material fracture toughness to assess the structural integrity of the vessel. The paper also include some parametric analyses to justify the methodology. (author)