[en] The effect of oxygen on stability of isothermal omega precipitates in Ti-29Nb-13Ta-4.6Zr was examined using X-ray powder diffraction, transmission electron microscopy, and atom probe tomography. Two alloys with 0.1 and 0.4 mass% oxygen were subjected to single step, and two-step annealing heat-treatments to respectively promote omega and alpha formation. After second step annealing, large volume fraction of omega precipitates was retained in 0.4 mass% O alloy while mainly alpha phase was observed in TNTZ-0.1O. The enhanced stability of omega in the higher oxygen containing TNTZ alloys questions the conventionally accepted understanding that oxygen destabilizes the omega phase in titanium alloys.