[en] About twelve thousand fuel pins for the JOYO core fuel were fabricated, and their end plug welding was inspected by X-ray radiography. The defect fractions were 0.2 percent for the lower end plugs and 1.8 percent for the upper, respectively. It had been known that the defect was due to ''line porosity''. In this study, the cause of the ''line porosity defect'' was investigated by the welding experiment performed on some dummy specimens of three different types; open end; closed end; and closed end with dummy pellets and a spring. The position of electrodes was varied for changing the arc gap from 0.3 mm to 1.2 mm. The experimental results are summarized in tables. The results showed that no defect was found in the open end type specimens even with the arc gap of 1.2 mm. Whereas in the other two types of specimens, the defect fraction of 60 to 75 percent was observed with the same arc gap. As for the effect of the arc gap, it was shown that 0.3 mm is the best among 0.3 mm, 0.5 mm and 1.2 mm. No defect was observed in the third type of specimens with the arc gap of 0.3 mm. In summary, it was found that the line porosity defect did not depend on the shape of the end plugs. It is considered to be dependent on both the structure of dummy fuel pins and the position of electrodes. (Aoki, K.)